Evaluation of a XVIII Century Steel Bar in the Cathedral of Mexico
שמור ב:
| הוצא לאור ב: | Journal of Failure Analysis and Prevention vol. 10, no. 2 (Apr 2010), p. 82 |
|---|---|
| מחבר ראשי: | |
| מחברים אחרים: | , |
| יצא לאור: |
Springer Nature B.V.
|
| גישה מקוונת: | Citation/Abstract Full Text Full Text - PDF |
| תגים: |
אין תגיות, היה/י הראשונ/ה לתייג את הרשומה!
|
MARC
| LEADER | 00000nab a2200000uu 4500 | ||
|---|---|---|---|
| 001 | 871498911 | ||
| 003 | UK-CbPIL | ||
| 022 | |a 1547-7029 | ||
| 022 | |a 1864-1245 | ||
| 022 | |a 1529-8159 | ||
| 024 | 7 | |a 10.1007/s11668-010-9325-z |2 doi | |
| 035 | |a 871498911 | ||
| 045 | 2 | |b d20100401 |b d20100430 | |
| 084 | |a 137831 |2 nlm | ||
| 100 | 1 | |a Noguez, M E | |
| 245 | 1 | |a Evaluation of a XVIII Century Steel Bar in the Cathedral of Mexico | |
| 260 | |b Springer Nature B.V. |c Apr 2010 | ||
| 513 | |a Feature | ||
| 520 | 3 | |a A cracked segment from a XVIII century steel bar was removed from the Cathedral of Mexico City for analysis in hopes of determining the source of the bar, its manufacturing process and the significance of several cracks. The historical and experimental analysis showed that the bar was manufactured by a puddling process typical of English steels and one crack was caused by lack of fusion when small bars were forge welded to form the bar used in the Cathedral and another crack was a fracture that also accompanied the forge welding process. The cracks developed during manufacture and were not the result of in-service degradation.[PUBLICATION ABSTRACT] | |
| 700 | 1 | |a Mojica, D | |
| 700 | 1 | |a Robert, T | |
| 773 | 0 | |t Journal of Failure Analysis and Prevention |g vol. 10, no. 2 (Apr 2010), p. 82 | |
| 786 | 0 | |d ProQuest |t Materials Science Database | |
| 856 | 4 | 1 | |3 Citation/Abstract |u https://www.proquest.com/docview/871498911/abstract/embedded/7BTGNMKEMPT1V9Z2?source=fedsrch |
| 856 | 4 | 0 | |3 Full Text |u https://www.proquest.com/docview/871498911/fulltext/embedded/7BTGNMKEMPT1V9Z2?source=fedsrch |
| 856 | 4 | 0 | |3 Full Text - PDF |u https://www.proquest.com/docview/871498911/fulltextPDF/embedded/7BTGNMKEMPT1V9Z2?source=fedsrch |